Zamak 7 vs. C34000 Brass
Zamak 7 belongs to the zinc alloys classification, while C34000 brass belongs to the copper alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is Zamak 7 and the bottom bar is C34000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 86 | |
| 100 |
| Poisson's Ratio | 0.25 | |
| 0.31 |
| Shear Modulus, GPa | 33 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 340 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 95 | |
| 120 |
| Melting Completion (Liquidus), °C | 390 | |
| 930 |
| Melting Onset (Solidus), °C | 380 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 27 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 38 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 24 |
| Density, g/cm3 | 6.4 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 57 | |
| 45 |
| Embodied Water, L/kg | 380 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 12 | |
| 11 to 22 |
| Strength to Weight: Bending, points | 15 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 43 | |
| 37 |
| Thermal Shock Resistance, points | 8.6 | |
| 11 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 3.5 to 4.3 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 62 to 65 |
| Iron (Fe), % | 0 to 0.075 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.0030 | |
| 0.8 to 1.5 |
| Magnesium (Mg), % | 0.0050 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0.0050 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 to 0.0010 | |
| 0 |
| Zinc (Zn), % | 95.3 to 96.5 | |
| 33 to 37.2 |
| Residuals, % | 0 | |
| 0 to 0.4 |