ZA-12 vs. CC764S Brass
ZA-12 belongs to the zinc alloys classification, while CC764S brass belongs to the copper alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ZA-12 and the bottom bar is CC764S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 89 to 100 | |
| 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 110 |
| Elongation at Break, % | 1.6 to 5.3 | |
| 15 |
| Poisson's Ratio | 0.26 | |
| 0.31 |
| Shear Modulus, GPa | 33 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 400 | |
| 680 |
| Tensile Strength: Yield (Proof), MPa | 210 to 320 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 130 |
| Melting Completion (Liquidus), °C | 430 | |
| 850 |
| Melting Onset (Solidus), °C | 380 | |
| 810 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 400 |
| Thermal Conductivity, W/m-K | 120 | |
| 94 |
| Thermal Expansion, µm/m-K | 24 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 36 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 23 |
| Density, g/cm3 | 6.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.9 |
| Embodied Energy, MJ/kg | 64 | |
| 49 |
| Embodied Water, L/kg | 440 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.0 to 20 | |
| 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 620 | |
| 390 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 24 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 22 |
| Thermal Diffusivity, mm2/s | 43 | |
| 30 |
| Thermal Shock Resistance, points | 9.4 to 14 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 10.5 to 11.5 | |
| 1.0 to 3.0 |
| Antimony (Sb), % | 0 | |
| 0 to 0.050 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Copper (Cu), % | 0.5 to 1.2 | |
| 52 to 66 |
| Iron (Fe), % | 0 to 0.075 | |
| 0.5 to 2.5 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 0.015 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 4.0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 to 3.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.060 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 to 0.3 |
| Zinc (Zn), % | 87.1 to 89 | |
| 20.7 to 50.2 |