ZA-27 vs. ASTM B617 Coin Silver
ZA-27 belongs to the zinc alloys classification, while ASTM B617 coin silver belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is ZA-27 and the bottom bar is ASTM B617 coin silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 75 |
| Elongation at Break, % | 2.0 to 4.5 | |
| 1.1 to 22 |
| Poisson's Ratio | 0.27 | |
| 0.37 |
| Shear Modulus, GPa | 31 | |
| 28 |
| Shear Strength, MPa | 230 to 330 | |
| 180 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 430 | |
| 290 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 120 |
| Melting Completion (Liquidus), °C | 480 | |
| 870 |
| Melting Onset (Solidus), °C | 380 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 530 | |
| 250 |
| Thermal Expansion, µm/m-K | 26 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 83 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 53 | |
| 72 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.6 | |
| 4.1 |
| Stiffness to Weight: Bending, points | 28 | |
| 14 |
| Strength to Weight: Axial, points | 22 to 24 | |
| 7.7 to 14 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 9.3 to 14 |
| Thermal Shock Resistance, points | 14 to 15 | |
| 14 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 25 to 28 | |
| 0 to 0.0050 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 to 0.050 |
| Copper (Cu), % | 2.0 to 2.5 | |
| 9.0 to 10.4 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 to 0.030 |
| Magnesium (Mg), % | 0.010 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 |
| Silver (Ag), % | 0 | |
| 89.6 to 91 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Zinc (Zn), % | 69.3 to 73 | |
| 0 to 0.060 |
| Residuals, % | 0 | |
| 0 to 0.060 |