ZA-8 vs. Titanium 15-3-3-3
ZA-8 belongs to the zinc alloys classification, while titanium 15-3-3-3 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ZA-8 and the bottom bar is titanium 15-3-3-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 85 to 86 | |
| 100 |
| Elongation at Break, % | 1.3 to 8.0 | |
| 5.7 to 8.0 |
| Fatigue Strength, MPa | 51 to 100 | |
| 610 to 710 |
| Poisson's Ratio | 0.26 | |
| 0.33 |
| Shear Modulus, GPa | 34 | |
| 39 |
| Shear Strength, MPa | 240 to 280 | |
| 660 to 810 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 370 | |
| 1120 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 210 to 290 | |
| 1100 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 430 |
| Melting Completion (Liquidus), °C | 400 | |
| 1620 |
| Melting Onset (Solidus), °C | 380 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 520 |
| Thermal Conductivity, W/m-K | 120 | |
| 8.1 |
| Thermal Expansion, µm/m-K | 23 | |
| 9.8 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 1.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 40 | |
| 2.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 40 |
| Density, g/cm3 | 6.3 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 59 |
| Embodied Energy, MJ/kg | 62 | |
| 950 |
| Embodied Water, L/kg | 420 | |
| 260 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.8 to 28 | |
| 78 to 89 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 32 |
| Strength to Weight: Axial, points | 9.3 to 17 | |
| 64 to 80 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 42 | |
| 3.2 |
| Thermal Shock Resistance, points | 7.6 to 13 | |
| 79 to 98 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 8.0 to 8.8 | |
| 2.5 to 3.5 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 0.8 to 1.3 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.075 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 |
| Magnesium (Mg), % | 0.015 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Silicon (Si), % | 0 to 0.045 | |
| 0 |
| Tin (Sn), % | 0 to 0.0030 | |
| 2.5 to 3.5 |
| Titanium (Ti), % | 0 | |
| 72.6 to 78.5 |
| Vanadium (V), % | 0 | |
| 14 to 16 |
| Zinc (Zn), % | 89.7 to 91.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |