ZA-8 vs. C46200 Brass
ZA-8 belongs to the zinc alloys classification, while C46200 brass belongs to the copper alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ZA-8 and the bottom bar is C46200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 85 to 86 | |
| 100 |
| Elongation at Break, % | 1.3 to 8.0 | |
| 17 to 34 |
| Poisson's Ratio | 0.26 | |
| 0.31 |
| Shear Modulus, GPa | 34 | |
| 40 |
| Shear Strength, MPa | 240 to 280 | |
| 240 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 370 | |
| 370 to 480 |
| Tensile Strength: Yield (Proof), MPa | 210 to 290 | |
| 120 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 120 |
| Melting Completion (Liquidus), °C | 400 | |
| 840 |
| Melting Onset (Solidus), °C | 380 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 380 |
| Thermal Conductivity, W/m-K | 120 | |
| 110 |
| Thermal Expansion, µm/m-K | 23 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 24 |
| Density, g/cm3 | 6.3 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 2.7 |
| Embodied Energy, MJ/kg | 62 | |
| 46 |
| Embodied Water, L/kg | 420 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.8 to 28 | |
| 69 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 490 | |
| 72 to 400 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 9.3 to 17 | |
| 13 to 16 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 42 | |
| 35 |
| Thermal Shock Resistance, points | 7.6 to 13 | |
| 12 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 8.0 to 8.8 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Copper (Cu), % | 0.8 to 1.3 | |
| 62 to 65 |
| Iron (Fe), % | 0 to 0.075 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 to 0.2 |
| Magnesium (Mg), % | 0.015 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.045 | |
| 0 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 89.7 to 91.2 | |
| 33.3 to 37.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |