Zinc-High Copper Rolled Zinc Alloy (Z40301)

Z40301 zinc is an otherwise-unclassified alloy of zinc. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. It has a moderately low heat capacity and a fairly high ductility among zinc alloys. The graph bars on the material properties cards below compare Z40301 zinc to other zinc alloys (top) and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

87 GPa 13 x 106 psi

Elongation at Break

60 %

Poisson's Ratio

0.25

Shear Modulus

35 GPa 5.1 x 106 psi

Tensile Strength: Ultimate (UTS)

190 MPa 27 x 103 psi

Tensile Strength: Yield (Proof)

150 MPa 22 x 103 psi

Thermal Properties

Latent Heat of Fusion

110 J/g

Maximum Temperature: Mechanical

90 °C 190 °F

Melting Completion (Liquidus)

410 °C 780 °F

Melting Onset (Solidus)

400 °C 750 °F

Specific Heat Capacity

390 J/kg-K 0.093 BTU/lb-°F

Thermal Conductivity

110 W/m-K 65 BTU/h-ft-°F

Thermal Expansion

26 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

27 % IACS

Electrical Conductivity: Equal Weight (Specific)

37 % IACS

Otherwise Unclassified Properties

Base Metal Price

12 % relative

Density

6.6 g/cm3 410 lb/ft3

Embodied Carbon

2.8 kg CO2/kg material

Embodied Energy

53 MJ/kg 23 x 103 BTU/lb

Embodied Water

340 L/kg 41 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

100 MJ/m3

Resilience: Unit (Modulus of Resilience)

130 kJ/m3

Stiffness to Weight: Axial

7.4 points

Stiffness to Weight: Bending

23 points

Strength to Weight: Axial

7.9 points

Strength to Weight: Bending

11 points

Thermal Diffusivity

44 mm2/s

Thermal Shock Resistance

5.9 points

Alloy Composition

Zinc (Zn)Zn 98.9 to 99.5
Copper (Cu)Cu 0.5 to 1.0
Titanium (Ti)Ti 0 to 0.040
Iron (Fe)Fe 0 to 0.010
Aluminum (Al)Al 0 to 0.010
Lead (Pb)Pb 0 to 0.010
Cadmium (Cd)Cd 0 to 0.0050
Tin (Sn)Sn 0 to 0.0030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ASTM B69: Standard Specification for Rolled Zinc

Corrosion Resistance of Zinc and Zinc Alloys, Frank C. Porter, 1994

Zinc Handbook: Properties, Processing, and Use In Design, Frank C. Porter, 1991

Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993