Z41321 Zinc vs. A444.0 Aluminum

Z41321 zinc belongs to the zinc alloys classification, while A444.0 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is A444.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
70
Elongation at Break, % 60
18
Poisson's Ratio 0.25
0.33
Shear Modulus, GPa 35
26
Tensile Strength: Ultimate (UTS), MPa 190
160
Tensile Strength: Yield (Proof), MPa 150
66

Thermal Properties

Latent Heat of Fusion, J/g 110
500
Maximum Temperature: Mechanical, °C 90
170
Melting Completion (Liquidus), °C 410
630
Melting Onset (Solidus), °C 400
590
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 110
160
Thermal Expansion, µm/m-K 26
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
41
Electrical Conductivity: Equal Weight (Specific), % IACS 37
140

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.5
Density, g/cm3 6.6
2.6
Embodied Carbon, kg CO2/kg material 2.8
7.9
Embodied Energy, MJ/kg 54
150
Embodied Water, L/kg 340
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
24
Resilience: Unit (Modulus of Resilience), kJ/m3 130
31
Stiffness to Weight: Axial, points 7.4
15
Stiffness to Weight: Bending, points 23
53
Strength to Weight: Axial, points 7.9
17
Strength to Weight: Bending, points 11
25
Thermal Diffusivity, mm2/s 44
68
Thermal Shock Resistance, points 5.9
7.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
91.6 to 93.5
Cadmium (Cd), % 0 to 0.0050
0
Copper (Cu), % 0.5 to 1.0
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 0.2
Lead (Pb), % 0 to 0.010
0
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.1
Silicon (Si), % 0
6.5 to 7.5
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0 to 0.2
Zinc (Zn), % 98.8 to 99.42
0 to 0.1
Residuals, % 0
0 to 0.15