Z41321 Zinc vs. ACI-ASTM CA28MWV Steel

Z41321 zinc belongs to the zinc alloys classification, while ACI-ASTM CA28MWV steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is ACI-ASTM CA28MWV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 60
11
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
76
Tensile Strength: Ultimate (UTS), MPa 190
1080
Tensile Strength: Yield (Proof), MPa 150
870

Thermal Properties

Latent Heat of Fusion, J/g 110
270
Maximum Temperature: Mechanical, °C 90
740
Melting Completion (Liquidus), °C 410
1470
Melting Onset (Solidus), °C 400
1430
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
25
Thermal Expansion, µm/m-K 26
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
4.6
Electrical Conductivity: Equal Weight (Specific), % IACS 37
5.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
11
Density, g/cm3 6.6
7.9
Embodied Carbon, kg CO2/kg material 2.8
3.1
Embodied Energy, MJ/kg 54
44
Embodied Water, L/kg 340
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 130
1920
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 7.9
38
Strength to Weight: Bending, points 11
30
Thermal Diffusivity, mm2/s 44
6.6
Thermal Shock Resistance, points 5.9
40

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.2 to 0.28
Chromium (Cr), % 0
11 to 12.5
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 0 to 0.010
81.4 to 85.8
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0.5 to 1.0
Molybdenum (Mo), % 0
0.9 to 1.3
Nickel (Ni), % 0
0.5 to 1.0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Tungsten (W), % 0
0.9 to 1.3
Vanadium (V), % 0
0.2 to 0.3
Zinc (Zn), % 98.8 to 99.42
0