Z41321 Zinc vs. ASTM A182 Grade F3V

Z41321 zinc belongs to the zinc alloys classification, while ASTM A182 grade F3V belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is ASTM A182 grade F3V.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 60
20
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
74
Tensile Strength: Ultimate (UTS), MPa 190
660
Tensile Strength: Yield (Proof), MPa 150
470

Thermal Properties

Latent Heat of Fusion, J/g 110
250
Maximum Temperature: Mechanical, °C 90
470
Melting Completion (Liquidus), °C 410
1470
Melting Onset (Solidus), °C 400
1430
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
39
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 12
4.2
Density, g/cm3 6.6
7.9
Embodied Carbon, kg CO2/kg material 2.8
2.3
Embodied Energy, MJ/kg 54
33
Embodied Water, L/kg 340
63

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
120
Resilience: Unit (Modulus of Resilience), kJ/m3 130
590
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
23
Strength to Weight: Bending, points 11
21
Thermal Diffusivity, mm2/s 44
10
Thermal Shock Resistance, points 5.9
19

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Boron (B), % 0
0.0010 to 0.0030
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.050 to 0.18
Chromium (Cr), % 0
2.8 to 3.2
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 0 to 0.010
94.4 to 95.7
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.1
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0.015 to 0.035
Vanadium (V), % 0
0.2 to 0.3
Zinc (Zn), % 98.8 to 99.42
0