Z41321 Zinc vs. AWS BNi-5

Z41321 zinc belongs to the zinc alloys classification, while AWS BNi-5 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is AWS BNi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
72
Tensile Strength: Ultimate (UTS), MPa 190
470

Thermal Properties

Latent Heat of Fusion, J/g 110
470
Melting Completion (Liquidus), °C 410
1140
Melting Onset (Solidus), °C 400
1080
Specific Heat Capacity, J/kg-K 390
510
Thermal Expansion, µm/m-K 26
12

Otherwise Unclassified Properties

Base Metal Price, % relative 12
55
Density, g/cm3 6.6
7.7
Embodied Carbon, kg CO2/kg material 2.8
8.9
Embodied Energy, MJ/kg 54
130
Embodied Water, L/kg 340
260

Common Calculations

Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 7.9
17
Strength to Weight: Bending, points 11
17
Thermal Shock Resistance, points 5.9
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
0 to 0.050
Boron (B), % 0
0 to 0.030
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
18.5 to 19.5
Cobalt (Co), % 0
0 to 0.1
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 0 to 0.010
0
Lead (Pb), % 0 to 0.010
0
Nickel (Ni), % 0
69.1 to 71.8
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0
9.8 to 10.5
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0 to 0.050
Zinc (Zn), % 98.8 to 99.42
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5