MakeItFrom.com
Menu (ESC)

Z41321 Zinc vs. AWS ENiCrMo-10

Z41321 zinc belongs to the zinc alloys classification, while AWS ENiCrMo-10 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is AWS ENiCrMo-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
220
Elongation at Break, % 60
28
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
84
Tensile Strength: Ultimate (UTS), MPa 190
710

Thermal Properties

Latent Heat of Fusion, J/g 110
320
Melting Completion (Liquidus), °C 410
1550
Melting Onset (Solidus), °C 400
1490
Specific Heat Capacity, J/kg-K 390
420
Thermal Conductivity, W/m-K 110
10
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 37
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 12
70
Density, g/cm3 6.6
8.9
Embodied Carbon, kg CO2/kg material 2.8
12
Embodied Energy, MJ/kg 54
160
Embodied Water, L/kg 340
300

Common Calculations

Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 7.9
22
Strength to Weight: Bending, points 11
20
Thermal Diffusivity, mm2/s 44
2.7
Thermal Shock Resistance, points 5.9
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
20 to 22.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0.5 to 1.0
0 to 0.5
Iron (Fe), % 0 to 0.010
2.0 to 6.0
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
12.5 to 14.5
Nickel (Ni), % 0
48.4 to 63
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.2
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0
0 to 0.35
Zinc (Zn), % 98.8 to 99.42
0
Residuals, % 0
0 to 0.5