Z41321 Zinc vs. EN 1.4611 Stainless Steel

Z41321 zinc belongs to the zinc alloys classification, while EN 1.4611 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is EN 1.4611 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 60
21
Poisson's Ratio 0.25
0.27
Shear Modulus, GPa 35
78
Tensile Strength: Ultimate (UTS), MPa 190
530
Tensile Strength: Yield (Proof), MPa 150
280

Thermal Properties

Latent Heat of Fusion, J/g 110
290
Maximum Temperature: Mechanical, °C 90
970
Melting Completion (Liquidus), °C 410
1440
Melting Onset (Solidus), °C 400
1390
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 110
21
Thermal Expansion, µm/m-K 26
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 37
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
11
Density, g/cm3 6.6
7.7
Embodied Carbon, kg CO2/kg material 2.8
2.5
Embodied Energy, MJ/kg 54
36
Embodied Water, L/kg 340
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
91
Resilience: Unit (Modulus of Resilience), kJ/m3 130
190
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 7.9
19
Strength to Weight: Bending, points 11
19
Thermal Diffusivity, mm2/s 44
5.7
Thermal Shock Resistance, points 5.9
18

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.050
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
19 to 22
Copper (Cu), % 0.5 to 1.0
0 to 0.5
Iron (Fe), % 0 to 0.010
73.3 to 80.8
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 0.5
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0.2 to 1.0
Zinc (Zn), % 98.8 to 99.42
0