Z41321 Zinc vs. EN 1.4886 Stainless Steel

Z41321 zinc belongs to the zinc alloys classification, while EN 1.4886 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is EN 1.4886 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 60
45
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
76
Tensile Strength: Ultimate (UTS), MPa 190
580
Tensile Strength: Yield (Proof), MPa 150
300

Thermal Properties

Latent Heat of Fusion, J/g 110
320
Maximum Temperature: Mechanical, °C 90
1100
Melting Completion (Liquidus), °C 410
1390
Melting Onset (Solidus), °C 400
1340
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 110
12
Thermal Expansion, µm/m-K 26
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 37
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 6.6
8.0
Embodied Carbon, kg CO2/kg material 2.8
5.4
Embodied Energy, MJ/kg 54
76
Embodied Water, L/kg 340
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
220
Resilience: Unit (Modulus of Resilience), kJ/m3 130
230
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
20
Strength to Weight: Bending, points 11
19
Thermal Diffusivity, mm2/s 44
3.1
Thermal Shock Resistance, points 5.9
14

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
17 to 20
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 0 to 0.010
38.7 to 49
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
33 to 37
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
1.0 to 2.0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Zinc (Zn), % 98.8 to 99.42
0