Z41321 Zinc vs. EN 2.4889 Nickel

Z41321 zinc belongs to the zinc alloys classification, while EN 2.4889 nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is EN 2.4889 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 60
39
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
77
Tensile Strength: Ultimate (UTS), MPa 190
720
Tensile Strength: Yield (Proof), MPa 150
270

Thermal Properties

Latent Heat of Fusion, J/g 110
350
Maximum Temperature: Mechanical, °C 90
1200
Melting Completion (Liquidus), °C 410
1350
Melting Onset (Solidus), °C 400
1300
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 110
13
Thermal Expansion, µm/m-K 26
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 37
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
42
Density, g/cm3 6.6
8.0
Embodied Carbon, kg CO2/kg material 2.8
6.9
Embodied Energy, MJ/kg 54
98
Embodied Water, L/kg 340
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
220
Resilience: Unit (Modulus of Resilience), kJ/m3 130
180
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
25
Strength to Weight: Bending, points 11
22
Thermal Diffusivity, mm2/s 44
3.4
Thermal Shock Resistance, points 5.9
19

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 0
26 to 29
Copper (Cu), % 0.5 to 1.0
0 to 0.3
Iron (Fe), % 0 to 0.010
21 to 25
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
45 to 50.4
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
2.5 to 3.0
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Zinc (Zn), % 98.8 to 99.42
0