Z41321 Zinc vs. Monel R-405

Z41321 zinc belongs to the zinc alloys classification, while Monel R-405 belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is Monel R-405.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
160
Elongation at Break, % 60
9.1 to 39
Poisson's Ratio 0.25
0.32
Shear Modulus, GPa 35
62
Tensile Strength: Ultimate (UTS), MPa 190
540 to 630
Tensile Strength: Yield (Proof), MPa 150
190 to 350

Thermal Properties

Latent Heat of Fusion, J/g 110
270
Maximum Temperature: Mechanical, °C 90
900
Melting Completion (Liquidus), °C 410
1350
Melting Onset (Solidus), °C 400
1300
Specific Heat Capacity, J/kg-K 390
430
Thermal Conductivity, W/m-K 110
23
Thermal Expansion, µm/m-K 26
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 37
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
50
Density, g/cm3 6.6
8.9
Embodied Carbon, kg CO2/kg material 2.8
7.9
Embodied Energy, MJ/kg 54
110
Embodied Water, L/kg 340
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
49 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 130
120 to 370
Stiffness to Weight: Axial, points 7.4
10
Stiffness to Weight: Bending, points 23
21
Strength to Weight: Axial, points 7.9
17 to 20
Strength to Weight: Bending, points 11
17 to 18
Thermal Diffusivity, mm2/s 44
5.9
Thermal Shock Resistance, points 5.9
17 to 20

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.3
Copper (Cu), % 0.5 to 1.0
28 to 34
Iron (Fe), % 0 to 0.010
0 to 2.5
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
63 to 72
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0.025 to 0.060
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Zinc (Zn), % 98.8 to 99.42
0