Z41321 Zinc vs. SAE-AISI 6150 Steel

Z41321 zinc belongs to the zinc alloys classification, while SAE-AISI 6150 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is SAE-AISI 6150 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 60
15 to 23
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
73
Tensile Strength: Ultimate (UTS), MPa 190
630 to 1200
Tensile Strength: Yield (Proof), MPa 150
420 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 110
250
Maximum Temperature: Mechanical, °C 90
420
Melting Completion (Liquidus), °C 410
1460
Melting Onset (Solidus), °C 400
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
46
Thermal Expansion, µm/m-K 26
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.3
Density, g/cm3 6.6
7.8
Embodied Carbon, kg CO2/kg material 2.8
2.0
Embodied Energy, MJ/kg 54
28
Embodied Water, L/kg 340
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
130 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 130
460 to 3590
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
22 to 43
Strength to Weight: Bending, points 11
21 to 32
Thermal Diffusivity, mm2/s 44
13
Thermal Shock Resistance, points 5.9
20 to 38

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.48 to 0.53
Chromium (Cr), % 0
0.8 to 1.1
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 0 to 0.010
96.7 to 97.7
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0.7 to 0.9
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Vanadium (V), % 0
0.15 to 0.3
Zinc (Zn), % 98.8 to 99.42
0