Z41321 Zinc vs. SAE-AISI O6 Steel

Z41321 zinc belongs to the zinc alloys classification, while SAE-AISI O6 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is SAE-AISI O6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
180
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
71
Tensile Strength: Ultimate (UTS), MPa 190
670 to 2070

Thermal Properties

Latent Heat of Fusion, J/g 110
260
Melting Completion (Liquidus), °C 410
1430
Melting Onset (Solidus), °C 400
1390
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 110
43
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.3
Density, g/cm3 6.6
7.7
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 54
21
Embodied Water, L/kg 340
47

Common Calculations

Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 7.9
24 to 74
Strength to Weight: Bending, points 11
22 to 47
Thermal Diffusivity, mm2/s 44
12
Thermal Shock Resistance, points 5.9
22 to 69

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
1.3 to 1.6
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0.5 to 1.0
0 to 0.25
Iron (Fe), % 0 to 0.010
94.6 to 97.7
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0.3 to 1.1
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.55 to 1.5
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Zinc (Zn), % 98.8 to 99.42
0