Z41321 Zinc vs. N08904 Stainless Steel

Z41321 zinc belongs to the zinc alloys classification, while N08904 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is N08904 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 60
38
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
79
Tensile Strength: Ultimate (UTS), MPa 190
540
Tensile Strength: Yield (Proof), MPa 150
240

Thermal Properties

Latent Heat of Fusion, J/g 110
300
Maximum Temperature: Mechanical, °C 90
1100
Melting Completion (Liquidus), °C 410
1440
Melting Onset (Solidus), °C 400
1390
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
12
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 37
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
32
Density, g/cm3 6.6
8.1
Embodied Carbon, kg CO2/kg material 2.8
5.8
Embodied Energy, MJ/kg 54
79
Embodied Water, L/kg 340
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
170
Resilience: Unit (Modulus of Resilience), kJ/m3 130
150
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
19
Strength to Weight: Bending, points 11
18
Thermal Diffusivity, mm2/s 44
3.1
Thermal Shock Resistance, points 5.9
12

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
19 to 23
Copper (Cu), % 0.5 to 1.0
1.0 to 2.0
Iron (Fe), % 0 to 0.010
38.8 to 53
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
23 to 28
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.035
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Zinc (Zn), % 98.8 to 99.42
0