Z21721 Zinc vs. 513.0 Aluminum

Z21721 zinc belongs to the zinc alloys classification, while 513.0 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is Z21721 zinc and the bottom bar is 513.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
68
Elongation at Break, % 40
5.7
Poisson's Ratio 0.25
0.33
Shear Modulus, GPa 35
26
Tensile Strength: Ultimate (UTS), MPa 150
200
Tensile Strength: Yield (Proof), MPa 120
120

Thermal Properties

Latent Heat of Fusion, J/g 110
390
Maximum Temperature: Mechanical, °C 90
170
Melting Completion (Liquidus), °C 410
640
Melting Onset (Solidus), °C 390
590
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 110
130
Thermal Expansion, µm/m-K 26
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
34
Electrical Conductivity: Equal Weight (Specific), % IACS 37
110

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.5
Density, g/cm3 6.6
2.7
Embodied Carbon, kg CO2/kg material 2.8
8.8
Embodied Energy, MJ/kg 53
150
Embodied Water, L/kg 340
1170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
9.8
Resilience: Unit (Modulus of Resilience), kJ/m3 88
100
Stiffness to Weight: Axial, points 7.3
14
Stiffness to Weight: Bending, points 22
50
Strength to Weight: Axial, points 6.4
20
Strength to Weight: Bending, points 9.6
28
Thermal Diffusivity, mm2/s 44
54
Thermal Shock Resistance, points 4.8
8.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0020
91.9 to 95.1
Cadmium (Cd), % 0 to 0.070
0
Copper (Cu), % 0 to 0.0050
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 0.4
Lead (Pb), % 0 to 1.0
0
Magnesium (Mg), % 0
3.5 to 4.5
Manganese (Mn), % 0
0 to 0.3
Silicon (Si), % 0
0 to 0.3
Titanium (Ti), % 0 to 0.020
0 to 0.2
Zinc (Zn), % 98.9 to 100
1.4 to 2.2
Residuals, % 0
0 to 0.15