Z40101 Zinc vs. 2024 Aluminum

Z40101 zinc belongs to the zinc alloys classification, while 2024 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is Z40101 zinc and the bottom bar is 2024 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
71
Elongation at Break, % 44
4.0 to 16
Poisson's Ratio 0.25
0.33
Shear Modulus, GPa 35
27
Tensile Strength: Ultimate (UTS), MPa 130
200 to 540
Tensile Strength: Yield (Proof), MPa 110
100 to 490

Thermal Properties

Latent Heat of Fusion, J/g 110
390
Maximum Temperature: Mechanical, °C 90
200
Melting Completion (Liquidus), °C 410
640
Melting Onset (Solidus), °C 400
500
Specific Heat Capacity, J/kg-K 390
880
Thermal Conductivity, W/m-K 110
120
Thermal Expansion, µm/m-K 26
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
30
Electrical Conductivity: Equal Weight (Specific), % IACS 37
90

Otherwise Unclassified Properties

Base Metal Price, % relative 11
11
Density, g/cm3 6.6
3.0
Embodied Carbon, kg CO2/kg material 2.8
8.3
Embodied Energy, MJ/kg 53
150
Embodied Water, L/kg 340
1140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
20 to 68
Resilience: Unit (Modulus of Resilience), kJ/m3 69
70 to 1680
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
46
Strength to Weight: Axial, points 5.7
18 to 50
Strength to Weight: Bending, points 8.9
25 to 49
Thermal Diffusivity, mm2/s 44
46
Thermal Shock Resistance, points 4.2
8.6 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
90.7 to 94.7
Cadmium (Cd), % 0 to 0.0050
0
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 0.080 to 0.4
3.8 to 4.9
Iron (Fe), % 0 to 0.010
0 to 0.5
Lead (Pb), % 0 to 0.010
0
Magnesium (Mg), % 0
1.2 to 1.8
Manganese (Mn), % 0
0.3 to 0.9
Silicon (Si), % 0
0 to 0.5
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0 to 0.020
0 to 0.15
Zinc (Zn), % 99.542 to 99.92
0 to 0.25
Zirconium (Zr), % 0
0 to 0.2
Residuals, % 0
0 to 0.15