Z40101 Zinc vs. CC380H Copper-nickel

Z40101 zinc belongs to the zinc alloys classification, while CC380H copper-nickel belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is Z40101 zinc and the bottom bar is CC380H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
120
Elongation at Break, % 44
26
Poisson's Ratio 0.25
0.34
Shear Modulus, GPa 35
47
Tensile Strength: Ultimate (UTS), MPa 130
310
Tensile Strength: Yield (Proof), MPa 110
120

Thermal Properties

Latent Heat of Fusion, J/g 110
220
Maximum Temperature: Mechanical, °C 90
220
Melting Completion (Liquidus), °C 410
1130
Melting Onset (Solidus), °C 400
1080
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 110
46
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
11
Electrical Conductivity: Equal Weight (Specific), % IACS 37
11

Otherwise Unclassified Properties

Base Metal Price, % relative 11
36
Density, g/cm3 6.6
8.9
Embodied Carbon, kg CO2/kg material 2.8
3.8
Embodied Energy, MJ/kg 53
58
Embodied Water, L/kg 340
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
65
Resilience: Unit (Modulus of Resilience), kJ/m3 69
59
Stiffness to Weight: Axial, points 7.4
7.8
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 5.7
9.8
Strength to Weight: Bending, points 8.9
12
Thermal Diffusivity, mm2/s 44
13
Thermal Shock Resistance, points 4.2
11

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.010
Cadmium (Cd), % 0 to 0.0050
0
Copper (Cu), % 0.080 to 0.4
84.5 to 89
Iron (Fe), % 0 to 0.010
1.0 to 1.8
Lead (Pb), % 0 to 0.010
0 to 0.030
Manganese (Mn), % 0
1.0 to 1.5
Nickel (Ni), % 0
9.0 to 11
Niobium (Nb), % 0
0 to 1.0
Silicon (Si), % 0
0 to 0.1
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0 to 0.020
0
Zinc (Zn), % 99.542 to 99.92
0 to 0.5