Z40101 Zinc vs. Solder Alloy 102

Z40101 zinc belongs to the zinc alloys classification, while solder alloy 102 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z40101 zinc and the bottom bar is solder alloy 102.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
38
Elongation at Break, % 44
48
Poisson's Ratio 0.25
0.39
Shear Modulus, GPa 35
14
Tensile Strength: Ultimate (UTS), MPa 130
31

Thermal Properties

Latent Heat of Fusion, J/g 110
46
Melting Completion (Liquidus), °C 410
180
Melting Onset (Solidus), °C 400
180
Specific Heat Capacity, J/kg-K 390
190
Thermal Conductivity, W/m-K 110
53
Thermal Expansion, µm/m-K 26
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
12
Electrical Conductivity: Equal Weight (Specific), % IACS 37
13

Otherwise Unclassified Properties

Density, g/cm3 6.6
8.8
Embodied Carbon, kg CO2/kg material 2.8
11
Embodied Energy, MJ/kg 53
180
Embodied Water, L/kg 340
930

Common Calculations

Stiffness to Weight: Axial, points 7.4
2.4
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 5.7
1.0
Strength to Weight: Bending, points 8.9
2.5
Thermal Diffusivity, mm2/s 44
32
Thermal Shock Resistance, points 4.2
2.4

Alloy Composition

Aluminum (Al), % 0 to 0.010
0 to 0.0010
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.050
Cadmium (Cd), % 0 to 0.0050
0 to 0.0020
Copper (Cu), % 0.080 to 0.4
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 0.020
Lead (Pb), % 0 to 0.010
36 to 37.5
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0 to 0.0030
62.5 to 63.5
Titanium (Ti), % 0 to 0.020
0
Zinc (Zn), % 99.542 to 99.92
0 to 0.0010