MakeItFrom.com
Menu (ESC)

Z40101 Zinc vs. C11100 Copper

Z40101 zinc belongs to the zinc alloys classification, while C11100 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is Z40101 zinc and the bottom bar is C11100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
120
Elongation at Break, % 44
1.5
Poisson's Ratio 0.25
0.34
Shear Modulus, GPa 35
44
Tensile Strength: Ultimate (UTS), MPa 130
460
Tensile Strength: Yield (Proof), MPa 110
420

Thermal Properties

Latent Heat of Fusion, J/g 110
210
Maximum Temperature: Mechanical, °C 90
200
Melting Completion (Liquidus), °C 410
1080
Melting Onset (Solidus), °C 400
1070
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 110
390
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
100
Electrical Conductivity: Equal Weight (Specific), % IACS 37
100

Otherwise Unclassified Properties

Base Metal Price, % relative 11
31
Density, g/cm3 6.6
9.0
Embodied Carbon, kg CO2/kg material 2.8
2.6
Embodied Energy, MJ/kg 53
41
Embodied Water, L/kg 340
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
6.6
Resilience: Unit (Modulus of Resilience), kJ/m3 69
750
Stiffness to Weight: Axial, points 7.4
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 5.7
14
Strength to Weight: Bending, points 8.9
15
Thermal Diffusivity, mm2/s 44
110
Thermal Shock Resistance, points 4.2
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Copper (Cu), % 0.080 to 0.4
99.9 to 100
Iron (Fe), % 0 to 0.010
0
Lead (Pb), % 0 to 0.010
0
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0 to 0.020
0
Zinc (Zn), % 99.542 to 99.92
0
Residuals, % 0
0 to 0.1