Z40101 Zinc vs. C82800 Copper
Z40101 zinc belongs to the zinc alloys classification, while C82800 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is Z40101 zinc and the bottom bar is C82800 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 120 |
| Elongation at Break, % | 44 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.25 | |
| 0.33 |
| Shear Modulus, GPa | 35 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 130 | |
| 670 to 1140 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 380 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 310 |
| Melting Completion (Liquidus), °C | 410 | |
| 930 |
| Melting Onset (Solidus), °C | 400 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 26 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.6 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 12 |
| Embodied Energy, MJ/kg | 53 | |
| 190 |
| Embodied Water, L/kg | 340 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 | |
| 590 to 4080 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 5.7 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 8.9 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 44 | |
| 36 |
| Thermal Shock Resistance, points | 4.2 | |
| 23 to 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.010 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 2.5 to 2.9 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.15 to 0.7 |
| Copper (Cu), % | 0.080 to 0.4 | |
| 94.6 to 97.2 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.35 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 to 0.12 |
| Zinc (Zn), % | 99.542 to 99.92 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |