Zircon vs. Forsterite
Both zircon and forsterite are oxide-based engineering ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is zircon and the bottom bar is forsterite.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.9 | |
| 2.1 to 3.1 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 8.8 | |
| 6.2 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.9 | |
| 7.9 |
| Flexural Strength, MPa | 450 | |
| 40 to 160 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 1.7 to 3.5 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 9.0 to 10 |