Zirconia vs. Aluminosilicate Glass

Zirconia belongs to the oxide-based engineering ceramics classification, while aluminosilicate glass belongs to the glass and glass-ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is zirconia and the bottom bar is aluminosilicate glass.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 5.7 to 6.0
2.4
Dielectric Constant (Relative Permittivity) At 1 MHz 28
6.3
Elastic (Young's, Tensile) Modulus, GPa 190 to 200
87
Fracture Toughness, MPa-m1/2 8.0 to 11
0.9
Stiffness to Weight: Axial, points 19
20
Stiffness to Weight: Bending, points 33 to 34
63