1/16-Hard 304LN Stainless Steel

1/16-hard AISI 304LN is AISI 304LN stainless steel in the 1/16-hard temper. It has the second lowest strength and highest ductility compared to the other variants of AISI 304LN stainless steel.

The graph bars on the material properties cards below compare 1/16-hard AISI 304LN to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

220

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

46 %

Fatigue Strength

320 MPa 47 x 103 psi

Poisson's Ratio

0.28

Shear Modulus

77 GPa 11 x 106 psi

Shear Strength

500 MPa 72 x 103 psi

Tensile Strength: Ultimate (UTS)

710 MPa 100 x 103 psi

Tensile Strength: Yield (Proof)

350 MPa 50 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

420 °C 790 °F

Maximum Temperature: Mechanical

960 °C 1760 °F

Melting Completion (Liquidus)

1420 °C 2600 °F

Melting Onset (Solidus)

1380 °C 2520 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

15 W/m-K 8.7 BTU/h-ft-°F

Thermal Expansion

16 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.4 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.7 % IACS

Otherwise Unclassified Properties

Base Metal Price

16 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

3.1 kg CO2/kg material

Embodied Energy

44 MJ/kg 19 x 103 BTU/lb

Embodied Water

150 L/kg 18 gal/lb

Common Calculations

PREN (Pitting Resistance)

21

Resilience: Ultimate (Unit Rupture Work)

270 MJ/m3

Resilience: Unit (Modulus of Resilience)

310 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

25 points

Strength to Weight: Bending

23 points

Thermal Diffusivity

4.0 mm2/s

Thermal Shock Resistance

16 points

Alloy Composition

Iron (Fe)Fe 65 to 73.9
Chromium (Cr)Cr 18 to 20
Nickel (Ni)Ni 8.0 to 12
Manganese (Mn)Mn 0 to 2.0
Silicon (Si)Si 0 to 0.75
Nitrogen (N)N 0.1 to 0.16
Phosphorus (P)P 0 to 0.045
Carbon (C)C 0 to 0.030
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar

Machining of Stainless Steels and Super Alloys: Traditional and Nontraditional Techniques, Helmi A. Youssef, 2016

ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A276: Standard Specification for Stainless Steel Bars and Shapes

Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012

ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels

Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002

Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011

Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984

ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994