1050A-H28 Aluminum
1050A-H28 aluminum is 1050A aluminum in the H28 temper. This is the strongest temper normally produced through the action of strain hardening followed by partial annealing. It is closely related to H18.
It has the second highest strength and second lowest ductility compared to the other variants of 1050A aluminum.
The graph bars on the material properties cards below compare 1050A-H28 aluminum to: 1000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
41
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
2.2 %
Fatigue Strength
50 MPa 7.3 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
90 MPa 13 x 103 psi
Tensile Strength: Ultimate (UTS)
160 MPa 23 x 103 psi
Tensile Strength: Yield (Proof)
130 MPa 18 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
660 °C 1220 °F
Melting Onset (Solidus)
650 °C 1190 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
230 W/m-K 130 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
59 % IACS
Electrical Conductivity: Equal Weight (Specific)
200 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.0 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.2 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1200 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
3.3 MJ/m3
Resilience: Unit (Modulus of Resilience)
120 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
16 points
Strength to Weight: Bending
24 points
Thermal Diffusivity
94 mm2/s
Thermal Shock Resistance
7.0 points
Alloy Composition
| Al | 99.5 to 100 | |
| Fe | 0 to 0.4 | |
| Si | 0 to 0.25 | |
| Zn | 0 to 0.070 | |
| Mn | 0 to 0.050 | |
| Ti | 0 to 0.050 | |
| Cu | 0 to 0.050 | |
| Mg | 0 to 0.050 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products