1060-H113 Aluminum
1060-H113 aluminum is 1060 aluminum in the H113 temper. This temper is a very specific variation on H112 that only applies to standard tube products. Prior to 1982, the distinction did not exist, and the same products would have been labeled as H112.
It has the lowest strength compared to the other variants of 1060 aluminum.
The graph bars on the material properties cards below compare 1060-H113 aluminum to: 1000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Tensile Strength: Ultimate (UTS)
67 MPa 9.7 x 103 psi
Tensile Strength: Yield (Proof)
17 MPa 2.5 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
660 °C 1210 °F
Melting Onset (Solidus)
650 °C 1190 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
230 W/m-K 140 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
62 % IACS
Electrical Conductivity: Equal Weight (Specific)
210 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Calomel Potential
-750 mV
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
160 MJ/kg 67 x 103 BTU/lb
Embodied Water
1200 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
0.57 to 37 MJ/m3
Resilience: Unit (Modulus of Resilience)
2.1 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
6.9 points
Strength to Weight: Bending
14 points
Thermal Diffusivity
96 mm2/s
Thermal Shock Resistance
3.0 points
Alloy Composition
| Al | 99.6 to 100 | |
| Fe | 0 to 0.35 | |
| Si | 0 to 0.25 | |
| Zn | 0 to 0.050 | |
| Cu | 0 to 0.050 | |
| V | 0 to 0.050 | |
| Mn | 0 to 0.030 | |
| Ti | 0 to 0.030 | |
| Mg | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes
Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
Aluminum Standards and Data, Aluminum Association Inc., 2013
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products