1100-H113 Aluminum

1100-H113 aluminum is 1100 aluminum in the H113 temper. This temper is a very specific variation on H112 that only applies to standard tube products. Prior to 1982, the distinction did not exist, and the same products would have been labeled as H112.

It has the lowest strength compared to the other variants of 1100 aluminum.

The graph bars on the material properties cards below compare 1100-H113 aluminum to: 1000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

69 GPa 10 x 106 psi

Poisson's Ratio

0.33

Shear Modulus

26 GPa 3.8 x 106 psi

Tensile Strength: Ultimate (UTS)

86 MPa 12 x 103 psi

Tensile Strength: Yield (Proof)

28 MPa 4.1 x 103 psi

Thermal Properties

Latent Heat of Fusion

400 J/g

Maximum Temperature: Mechanical

180 °C 360 °F

Melting Completion (Liquidus)

660 °C 1210 °F

Melting Onset (Solidus)

640 °C 1190 °F

Specific Heat Capacity

900 J/kg-K 0.22 BTU/lb-°F

Thermal Conductivity

220 W/m-K 130 BTU/h-ft-°F

Thermal Expansion

24 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

59 % IACS

Electrical Conductivity: Equal Weight (Specific)

190 % IACS

Otherwise Unclassified Properties

Base Metal Price

9.0 % relative

Calomel Potential

-740 mV

Density

2.7 g/cm3 170 lb/ft3

Embodied Carbon

8.2 kg CO2/kg material

Embodied Energy

150 MJ/kg 66 x 103 BTU/lb

Embodied Water

1190 L/kg 140 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

0.76 to 52 MJ/m3

Resilience: Unit (Modulus of Resilience)

5.7 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

8.7 points

Strength to Weight: Bending

16 points

Thermal Diffusivity

90 mm2/s

Thermal Shock Resistance

3.7 points

Alloy Composition

Aluminum (Al)Al 99 to 99.95
Silicon (Si)Si 0 to 1.0
Iron (Fe)Fe 0 to 1.0
Copper (Cu)Cu 0.050 to 0.2
Zinc (Zn)Zn 0 to 0.1
Manganese (Mn)Mn 0 to 0.050
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications

ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes

ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube

Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014.

ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate

Aluminum Standards and Data, Aluminum Association Inc., 2013

EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products

Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993