1350-H142 Aluminum

1350-H142 aluminum is 1350 aluminum in the H142 temper. The graph bars on the material properties cards below compare 1350-H142 aluminum to: 1000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

68 GPa 9.9 x 106 psi

Poisson's Ratio

0.33

Shear Modulus

26 GPa 3.7 x 106 psi

Tensile Strength: Ultimate (UTS)

100 MPa 15 x 103 psi

Thermal Properties

Latent Heat of Fusion

400 J/g

Maximum Temperature: Mechanical

170 °C 340 °F

Melting Completion (Liquidus)

660 °C 1210 °F

Melting Onset (Solidus)

650 °C 1190 °F

Specific Heat Capacity

900 J/kg-K 0.22 BTU/lb-°F

Thermal Conductivity

230 W/m-K 140 BTU/h-ft-°F

Thermal Expansion

24 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

62 % IACS

Electrical Conductivity: Equal Weight (Specific)

210 % IACS

Otherwise Unclassified Properties

Base Metal Price

9.5 % relative

Calomel Potential

-740 mV

Density

2.7 g/cm3 170 lb/ft3

Embodied Carbon

8.3 kg CO2/kg material

Embodied Energy

160 MJ/kg 67 x 103 BTU/lb

Embodied Water

1200 L/kg 140 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

0.77 to 54 MJ/m3

Resilience: Unit (Modulus of Resilience)

4.4 to 200 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

10 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

96 mm2/s

Thermal Shock Resistance

4.4 points

Alloy Composition

Aluminum (Al)Al 99.5 to 100
Iron (Fe)Fe 0 to 0.4
Silicon (Si)Si 0 to 0.1
Boron (B)B 0 to 0.050
Zinc (Zn)Zn 0 to 0.050
Copper (Cu)Cu 0 to 0.050
Gallium (Ga)Ga 0 to 0.030
Titanium (Ti)Ti 0 to 0.020
Vanadium (V)V 0 to 0.020
Manganese (Mn)Mn 0 to 0.010
Chromium (Cr)Cr 0 to 0.010
Residualsres. 0 to 0.1

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM B609: Standard Specification for Aluminum 1350 Round Wire, Annealed and Intermediate Tempers, for Electrical Purposes

ASTM B230: Standard Specification for Aluminum 1350-H19 Wire for Electrical Purposes

ASTM B233: Standard Specification for Aluminum 1350 Drawing Stock for Electrical Purposes

Handbook of Aluminum Bonding Technology and Data, J. D. Minford, 1993

Aluminum Standards and Data, Aluminum Association Inc., 2013

EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products

Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993