2011-T3 Aluminum
2011-T3 aluminum is 2011 aluminum in the T3 temper. To achieve this temper, the metal is solution heat-treated, strain hardened, then naturally aged. The graph bars on the material properties cards below compare 2011-T3 aluminum to: 2000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
95
Elastic (Young's, Tensile) Modulus
71 GPa 10 x 106 psi
Elongation at Break
12 %
Fatigue Strength
120 MPa 18 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
27 GPa 3.9 x 106 psi
Shear Strength
220 MPa 32 x 103 psi
Tensile Strength: Ultimate (UTS)
360 MPa 52 x 103 psi
Tensile Strength: Yield (Proof)
280 MPa 40 x 103 psi
Thermal Properties
Latent Heat of Fusion
390 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
640 °C 1190 °F
Melting Onset (Solidus)
540 °C 1000 °F
Specific Heat Capacity
870 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
150 W/m-K 87 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
39 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
11 % relative
Density
3.1 g/cm3 200 lb/ft3
Embodied Carbon
7.9 kg CO2/kg material
Embodied Energy
150 MJ/kg 63 x 103 BTU/lb
Embodied Water
1150 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
39 MJ/m3
Resilience: Unit (Modulus of Resilience)
540 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
44 points
Strength to Weight: Axial
32 points
Strength to Weight: Bending
36 points
Thermal Diffusivity
56 mm2/s
Thermal Shock Resistance
16 points
Alloy Composition
| Al | 91.3 to 94.6 | |
| Cu | 5.0 to 6.0 | |
| Pb | 0.2 to 0.6 | |
| Bi | 0.2 to 0.6 | |
| Fe | 0 to 0.7 | |
| Si | 0 to 0.4 | |
| Zn | 0 to 0.3 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes
ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993