3/4-Hard (H03) C27000 Brass

H03 C27000 brass is C27000 brass in the H03 (3/4 hard) temper. The graph bars on the material properties cards below compare H03 C27000 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

110 GPa 15 x 106 psi

Poisson's Ratio

0.31

Rockwell B Hardness

75

Rockwell Superficial 30T Hardness

68

Shear Modulus

40 GPa 5.9 x 106 psi

Tensile Strength: Ultimate (UTS)

460 MPa 67 x 103 psi

Thermal Properties

Latent Heat of Fusion

180 J/g

Maximum Temperature: Mechanical

130 °C 270 °F

Melting Completion (Liquidus)

930 °C 1710 °F

Melting Onset (Solidus)

900 °C 1660 °F

Specific Heat Capacity

390 J/kg-K 0.092 BTU/lb-°F

Thermal Conductivity

120 W/m-K 67 BTU/h-ft-°F

Thermal Expansion

20 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

27 % IACS

Electrical Conductivity: Equal Weight (Specific)

30 % IACS

Otherwise Unclassified Properties

Base Metal Price

24 % relative

Density

8.1 g/cm3 510 lb/ft3

Embodied Carbon

2.7 kg CO2/kg material

Embodied Energy

45 MJ/kg 19 x 103 BTU/lb

Embodied Water

320 L/kg 38 gal/lb

Common Calculations

Stiffness to Weight: Axial

7.2 points

Stiffness to Weight: Bending

19 points

Strength to Weight: Axial

16 points

Strength to Weight: Bending

16 points

Thermal Diffusivity

37 mm2/s

Thermal Shock Resistance

15 points

Alloy Composition

Copper (Cu)Cu 63 to 68.5
Zinc (Zn)Zn 31 to 37
Iron (Fe)Fe 0 to 0.1
Lead (Pb)Pb 0 to 0.070
Residualsres. 0 to 0.3

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM B134: Standard Specification for Brass Wire

ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001