# 3/4-Hard (H03) C41300 Brass

H03 C41300 brass is C41300 brass in the H03 (3/4 hard) temper. The graph bars on the material properties cards below compare H03 C41300 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

## Mechanical Properties

Elastic (Young's, Tensile) Modulus

110 *GPa* 16 *x 10 ^{6} psi*

Elongation at Break

6.0 *%*

Poisson's Ratio

0.33

Rockwell B Hardness

76

Rockwell Superficial 30T Hardness

70

Shear Modulus

42 *GPa* 6.1 *x 10 ^{6} psi*

Shear Strength

300 *MPa* 44 *x 10 ^{3} psi*

Tensile Strength: Ultimate (UTS)

480 *MPa* 70 *x 10 ^{3} psi*

Tensile Strength: Yield (Proof)

480 *MPa* 69 *x 10 ^{3} psi*

## Thermal Properties

Latent Heat of Fusion

200 *J/g*

Maximum Temperature: Mechanical

180 *°C* 360 *°F*

Melting Completion (Liquidus)

1040 *°C* 1900 *°F*

Melting Onset (Solidus)

1010 *°C* 1850 *°F*

Specific Heat Capacity

380 *J/kg-K* 0.092 *BTU/lb-°F*

Thermal Conductivity

130 *W/m-K* 77 *BTU/h-ft-°F*

Thermal Expansion

18 *µm/m-K*

## Electrical Properties

Electrical Conductivity: Equal Volume

30 *% IACS*

Electrical Conductivity: Equal Weight (Specific)

31 *% IACS*

## Otherwise Unclassified Properties

Base Metal Price

29 *% relative*

Density

8.7 *g/cm ^{3}* 550

*lb/ft*

^{3}Embodied Carbon

2.7 *kg CO _{2}/kg material*

Embodied Energy

44 *MJ/kg* 19 *x 10 ^{3} BTU/lb*

Embodied Water

320 *L/kg* 38 *gal/lb*

## Common Calculations

Resilience: Ultimate (Unit Rupture Work)

29 *MJ/m ^{3}*

Resilience: Unit (Modulus of Resilience)

1000 *kJ/m ^{3}*

Stiffness to Weight: Axial

7.2 *points*

Stiffness to Weight: Bending

18 *points*

Strength to Weight: Axial

15 *points*

Strength to Weight: Bending

16 *points*

Thermal Diffusivity

40 *mm ^{2}/s*

Thermal Shock Resistance

17 *points*

## Alloy Composition

Cu | 89 to 93 | |

Zn | 5.1 to 10.3 | |

Sn | 0.7 to 1.3 | |

Pb | 0 to 0.1 | |

Fe | 0 to 0.050 | |

res. | 0 to 0.5 |

All values are % weight. Ranges represent what is permitted under applicable standards.