5052-H22 Aluminum

5052-H22 aluminum is 5052 aluminum in the H22 temper. To achieve this temper, the metal is strain hardened, and then partially annealed, to a strength that is roughly a quarter of the way between annealed (O) and full-hard (H28).

The graph bars on the material properties cards below compare 5052-H22 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

61

Elastic (Young's, Tensile) Modulus

68 GPa 9.9 x 106 psi

Elongation at Break

9.3 %

Fatigue Strength

130 MPa 19 x 103 psi

Poisson's Ratio

0.33

Shear Modulus

26 GPa 3.7 x 106 psi

Shear Strength

140 MPa 20 x 103 psi

Tensile Strength: Ultimate (UTS)

230 MPa 34 x 103 psi

Tensile Strength: Yield (Proof)

170 MPa 25 x 103 psi

Thermal Properties

Latent Heat of Fusion

400 J/g

Maximum Temperature: Mechanical

190 °C 370 °F

Melting Completion (Liquidus)

650 °C 1200 °F

Melting Onset (Solidus)

610 °C 1120 °F

Specific Heat Capacity

900 J/kg-K 0.22 BTU/lb-°F

Thermal Conductivity

140 W/m-K 80 BTU/h-ft-°F

Thermal Expansion

24 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

35 % IACS

Electrical Conductivity: Equal Weight (Specific)

120 % IACS

Otherwise Unclassified Properties

Base Metal Price

9.5 % relative

Calomel Potential

-760 mV

Density

2.7 g/cm3 170 lb/ft3

Embodied Carbon

8.6 kg CO2/kg material

Embodied Energy

150 MJ/kg 66 x 103 BTU/lb

Embodied Water

1190 L/kg 140 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

20 MJ/m3

Resilience: Unit (Modulus of Resilience)

210 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

31 points

Thermal Diffusivity

57 mm2/s

Thermal Shock Resistance

10 points

Alloy Composition

Aluminum (Al)Al 95.8 to 97.7
Magnesium (Mg)Mg 2.2 to 2.8
Chromium (Cr)Cr 0.15 to 0.35
Iron (Fe)Fe 0 to 0.4
Silicon (Si)Si 0 to 0.25
Manganese (Mn)Mn 0 to 0.1
Zinc (Zn)Zn 0 to 0.1
Copper (Cu)Cu 0 to 0.1
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube

Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014.

EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties

ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate

EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties

EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties

Aluminum Standards and Data, Aluminum Association Inc., 2013

ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993

ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties

EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products