5083-H24 Aluminum

5083-H24 aluminum is 5083 aluminum in the H24 temper. To achieve this temper, the metal is strain hardened, and then partially annealed, to a strength that is roughly halfway between annealed (O) and full-hard (H28).

The graph bars on the material properties cards below compare 5083-H24 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

99

Elastic (Young's, Tensile) Modulus

68 GPa 9.9 x 106 psi

Elongation at Break

4.5 %

Fatigue Strength

140 MPa 20 x 103 psi

Poisson's Ratio

0.33

Shear Modulus

26 GPa 3.7 x 106 psi

Shear Strength

210 MPa 30 x 103 psi

Tensile Strength: Ultimate (UTS)

360 MPa 52 x 103 psi

Tensile Strength: Yield (Proof)

270 MPa 40 x 103 psi

Thermal Properties

Latent Heat of Fusion

400 J/g

Maximum Temperature: Corrosion

65 °C 150 °F

Maximum Temperature: Mechanical

190 °C 370 °F

Melting Completion (Liquidus)

640 °C 1180 °F

Melting Onset (Solidus)

580 °C 1080 °F

Specific Heat Capacity

900 J/kg-K 0.22 BTU/lb-°F

Thermal Conductivity

120 W/m-K 68 BTU/h-ft-°F

Thermal Expansion

24 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

29 % IACS

Electrical Conductivity: Equal Weight (Specific)

96 % IACS

Otherwise Unclassified Properties

Base Metal Price

9.5 % relative

Calomel Potential

-780 mV

Density

2.7 g/cm3 170 lb/ft3

Embodied Carbon

8.9 kg CO2/kg material

Embodied Energy

150 MJ/kg 66 x 103 BTU/lb

Embodied Water

1170 L/kg 140 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

15 MJ/m3

Resilience: Unit (Modulus of Resilience)

550 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

37 points

Strength to Weight: Bending

42 points

Thermal Diffusivity

48 mm2/s

Thermal Shock Resistance

16 points

Alloy Composition

Aluminum (Al)Al 92.4 to 95.6
Magnesium (Mg)Mg 4.0 to 4.9
Manganese (Mn)Mn 0.4 to 1.0
Silicon (Si)Si 0 to 0.4
Iron (Fe)Fe 0 to 0.4
Chromium (Cr)Cr 0.050 to 0.25
Zinc (Zn)Zn 0 to 0.25
Titanium (Ti)Ti 0 to 0.15
Copper (Cu)Cu 0 to 0.1
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM B928: Standard Specification for High Magnesium Aluminum-Alloy Sheet and Plate for Marine Service

ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube

Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014.

EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties

ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate

EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties

EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties

Aluminum Standards and Data, Aluminum Association Inc., 2013

ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993

EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products