5254-H28 Aluminum
5254-H28 aluminum is 5254 aluminum in the H28 temper. This is the strongest temper normally produced through the action of strain hardening followed by partial annealing. It is closely related to H18. It has the lowest ductility compared to the other variants of 5254 aluminum.
The graph bars on the material properties cards below compare 5254-H28 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
68 GPa 9.8 x 106 psi
Elongation at Break
3.4 %
Fatigue Strength
110 MPa 16 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
200 MPa 29 x 103 psi
Tensile Strength: Ultimate (UTS)
350 MPa 50 x 103 psi
Tensile Strength: Yield (Proof)
270 MPa 40 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
640 °C 1190 °F
Melting Onset (Solidus)
590 °C 1100 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
130 W/m-K 72 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
32 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.8 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
11 MJ/m3
Resilience: Unit (Modulus of Resilience)
550 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
51 points
Strength to Weight: Axial
36 points
Strength to Weight: Bending
41 points
Thermal Diffusivity
52 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Al | 94.4 to 96.8 | |
| Mg | 3.1 to 3.9 | |
| Cr | 0.15 to 0.35 | |
| Si | 0 to 0.45 | |
| Fe | 0 to 0.45 | |
| Zn | 0 to 0.2 | |
| Ti | 0 to 0.050 | |
| Cu | 0 to 0.050 | |
| Mn | 0 to 0.010 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
Aluminum Standards and Data, Aluminum Association Inc., 2013
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993