6351-O Aluminum
6351-O aluminum is 6351 aluminum in the annealed condition. The graph bars on the material properties cards below compare 6351-O aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
16 %
Fatigue Strength
98 MPa 14 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
86 MPa 12 x 103 psi
Tensile Strength: Ultimate (UTS)
140 MPa 20 x 103 psi
Tensile Strength: Yield (Proof)
95 MPa 14 x 103 psi
Thermal Properties
Latent Heat of Fusion
410 J/g
Maximum Temperature: Mechanical
160 °C 320 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
570 °C 1060 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
180 W/m-K 100 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
46 % IACS
Electrical Conductivity: Equal Weight (Specific)
150 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
20 MJ/m3
Resilience: Unit (Modulus of Resilience)
65 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
14 points
Strength to Weight: Bending
22 points
Thermal Diffusivity
72 mm2/s
Thermal Shock Resistance
6.2 points
Alloy Composition
Al | 96 to 98.5 | |
Si | 0.7 to 1.3 | |
Mn | 0.4 to 0.8 | |
Mg | 0.4 to 0.8 | |
Fe | 0 to 0.5 | |
Ti | 0 to 0.2 | |
Zn | 0 to 0.2 | |
Cu | 0 to 0.1 | |
res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993