6463-T5 Aluminum
6463-T5 aluminum is 6463 aluminum in the T5 temper. To achieve this temper, the metal is artificially aged until it meets standard mechanical property requirements. It has the second lowest ductility compared to the other variants of 6463 aluminum.
The graph bars on the material properties cards below compare 6463-T5 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
60
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
10 %
Fatigue Strength
70 MPa 10 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
120 MPa 17 x 103 psi
Tensile Strength: Ultimate (UTS)
180 MPa 26 x 103 psi
Tensile Strength: Yield (Proof)
130 MPa 20 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
160 °C 320 °F
Melting Completion (Liquidus)
660 °C 1210 °F
Melting Onset (Solidus)
620 °C 1140 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
210 W/m-K 120 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
55 % IACS
Electrical Conductivity: Equal Weight (Specific)
180 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
17 MJ/m3
Resilience: Unit (Modulus of Resilience)
130 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
18 points
Strength to Weight: Bending
26 points
Thermal Diffusivity
86 mm2/s
Thermal Shock Resistance
7.9 points
Alloy Composition
| Al | 97.9 to 99.4 | |
| Mg | 0.45 to 0.9 | |
| Si | 0.2 to 0.6 | |
| Cu | 0 to 0.2 | |
| Fe | 0 to 0.15 | |
| Mn | 0 to 0.050 | |
| Zn | 0 to 0.050 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products