ASTM A27 Grade 70-36 (485-250, J03501) Cast Carbon Steel

ASTM A27 grade 70-36 is a type of ASTM A27 cast steel. Cited properties are appropriate for the normalized condition. It has the highest strength compared to the other variants of ASTM A27 cast steel. The graph bars on the material properties cards below compare ASTM A27 grade 70-36 to: cast carbon steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

25 %

Fatigue Strength

200 MPa 30 x 103 psi

Poisson's Ratio

0.29

Reduction in Area

34 %

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

550 MPa 80 x 103 psi

Tensile Strength: Yield (Proof)

280 MPa 41 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

52 W/m-K 30 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.0 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.1 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.8 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

18 MJ/kg 7.9 x 103 BTU/lb

Embodied Water

45 L/kg 5.4 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

120 MJ/m3

Resilience: Unit (Modulus of Resilience)

210 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

20 points

Strength to Weight: Bending

19 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

18 points

Alloy Composition

Iron (Fe)Fe 98 to 100
Silicon (Si)Si 0 to 0.8
Manganese (Mn)Mn 0 to 0.7
Carbon (C)C 0 to 0.35
Sulfur (S)S 0 to 0.060
Phosphorus (P)P 0 to 0.050

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ASTM A27: Standard Specification for Steel Castings, Carbon, for General Application

Carbon Steel Handbook, D. Gandy, 2007

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015