ASTM A439 Type D-5B (S-NiCr 35 3, F43007) Cast Iron

ASTM A439 type D-5B is a type of austenitic nodular cast iron. Cited properties are appropriate for the stress relieved condition. ASTM A439 Type D-5B is the ASTM designation for this material. F43007 is the UNS number. Additionally, the AFNOR (French) designation is FGS Ni35 Cr3.

The graph bars on the material properties cards below compare ASTM A439 type D-5B to: cast irons (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

170

Elastic (Young's, Tensile) Modulus

180 GPa 27 x 106 psi

Elongation at Break

6.8 %

Poisson's Ratio

0.3

Shear Modulus

71 GPa 10 x 106 psi

Tensile Strength: Ultimate (UTS)

430 MPa 63 x 103 psi

Tensile Strength: Yield (Proof)

240 MPa 34 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Melting Completion (Liquidus)

1390 °C 2530 °F

Melting Onset (Solidus)

1340 °C 2450 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Expansion

13 µm/m-K

Otherwise Unclassified Properties

Base Metal Price

25 % relative

Density

8.0 g/cm3 500 lb/ft3

Embodied Carbon

4.8 kg CO2/kg material

Embodied Energy

66 MJ/kg 29 x 103 BTU/lb

Embodied Water

120 L/kg 14 gal/lb

Common Calculations

PREN (Pitting Resistance)

2.5

Resilience: Ultimate (Unit Rupture Work)

25 MJ/m3

Resilience: Unit (Modulus of Resilience)

150 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

15 points

Strength to Weight: Bending

16 points

Thermal Shock Resistance

13 points

Alloy Composition

Iron (Fe)Fe 54.7 to 63
Nickel (Ni)Ni 34 to 36
Chromium (Cr)Cr 2.0 to 3.0
Silicon (Si)Si 1.0 to 2.8
Carbon (C)C 0 to 2.4
Manganese (Mn)Mn 0 to 1.0
Phosphorus (P)P 0 to 0.080

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ASTM A439: Standard Specification for Austenitic Ductile Iron Castings

ISO 2892: Austenitic Cast Irons - Classification

Cast Iron: Physical and Engineering Properties, Harold T. Angus, 1976

Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008