AWS BVAg-30 (P07687) Vacuum Service Filler Metal

AWS BVAg-30 is a silver-based filler metal for brazing. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. BVAg-30 is the AWS designation for this material. P07687 is the UNS number.

It has a moderately high density and a fairly high melting temperature among silver-based braze fillers.

The graph bars on the material properties cards below compare AWS BVAg-30 to: silver-based braze fillers (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Thermal Properties

Brazing Temperature

810 to 930 °C 1490 to 1700 °F

Latent Heat of Fusion

140 J/g

Melting Completion (Liquidus)

810 °C 1490 °F

Melting Onset (Solidus)

810 °C 1480 °F

Specific Heat Capacity

280 J/kg-K 0.066 BTU/lb-°F

Thermal Expansion

19 µm/m-K

Other Material Properties


10 g/cm3 630 lb/ft3

Elastic (Young's, Tensile) Modulus

86 GPa 12 x 106 psi

Poisson's Ratio


Shear Modulus

31 GPa 4.6 x 106 psi

Tensile Strength: Ultimate (UTS)

170 MPa 25 x 103 psi

Common Calculations

Stiffness to Weight: Axial

4.7 points

Stiffness to Weight: Bending

14 points

Strength to Weight: Axial

4.7 points

Strength to Weight: Bending

6.7 points

Thermal Shock Resistance

7.6 points

Alloy Composition

Silver (Ag)Ag 67 to 69
Copper (Cu)Cu 25.5 to 28.5
Palladium (Pd)Pd 4.5 to 5.5
Carbon (C)C 0 to 0.0050
Phosphorus (P)P 0 to 0.0020
Lead (Pb)Pb 0 to 0.0020
Zinc (Zn)Zn 0 to 0.0010
Cadmium (Cd)Cd 0 to 0.0010

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

AWS A5.8: Specification for Filler Metals for Brazing and Braze Welding