Annealed 202 Stainless Steel
Annealed AISI 202 is AISI 202 stainless steel in the annealed condition. The graph bars on the material properties cards below compare annealed AISI 202 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
210
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
45 %
Fatigue Strength
290 MPa 42 x 103 psi
Poisson's Ratio
0.28
Reduction in Area
57 %
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
490 MPa 71 x 103 psi
Tensile Strength: Ultimate (UTS)
700 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
310 MPa 45 x 103 psi
Thermal Properties
Latent Heat of Fusion
290 J/g
Maximum Temperature: Corrosion
410 °C 780 °F
Maximum Temperature: Mechanical
910 °C 1680 °F
Melting Completion (Liquidus)
1400 °C 2560 °F
Melting Onset (Solidus)
1360 °C 2480 °F
Specific Heat Capacity
480 J/kg-K 0.12 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.7 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.9 % IACS
Otherwise Unclassified Properties
Base Metal Price
13 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
2.8 kg CO2/kg material
Embodied Energy
40 MJ/kg 17 x 103 BTU/lb
Embodied Water
150 L/kg 18 gal/lb
Common Calculations
PREN (Pitting Resistance)
20
Resilience: Ultimate (Unit Rupture Work)
260 MJ/m3
Resilience: Unit (Modulus of Resilience)
250 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
4.0 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Fe | 63.5 to 71.5 | |
| Cr | 17 to 19 | |
| Mn | 7.5 to 10 | |
| Ni | 4.0 to 6.0 | |
| Si | 0 to 1.0 | |
| N | 0 to 0.25 | |
| C | 0 to 0.15 | |
| P | 0 to 0.060 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A473: Standard Specification for Stainless Steel Forgings
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015