Annealed 301 Stainless Steel
Annealed AISI 301 is AISI 301 stainless steel in the annealed condition. It has the lowest strength compared to the other variants of AISI 301 stainless steel. The graph bars on the material properties cards below compare annealed AISI 301 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
190
Elastic (Young's, Tensile) Modulus
200 GPa 28 x 106 psi
Elongation at Break
46 %
Fatigue Strength
210 MPa 31 x 103 psi
Poisson's Ratio
0.28
Rockwell B Hardness
82
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
410 MPa 60 x 103 psi
Tensile Strength: Ultimate (UTS)
590 MPa 85 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 33 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
410 °C 770 °F
Maximum Temperature: Mechanical
840 °C 1540 °F
Melting Completion (Liquidus)
1420 °C 2590 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
16 W/m-K 9.0 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
13 % relative
Calomel Potential
-70 mV
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
39 MJ/kg 17 x 103 BTU/lb
Embodied Water
130 L/kg 16 gal/lb
Common Calculations
PREN (Pitting Resistance)
18
Resilience: Ultimate (Unit Rupture Work)
210 MJ/m3
Resilience: Unit (Modulus of Resilience)
130 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Thermal Diffusivity
4.2 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Fe | 70.7 to 78 | |
| Cr | 16 to 18 | |
| Ni | 6.0 to 8.0 | |
| Mn | 0 to 2.0 | |
| Si | 0 to 1.0 | |
| C | 0 to 0.15 | |
| N | 0 to 0.1 | |
| P | 0 to 0.045 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010