Annealed 8630 Ni-Cr-Mo Steel

Annealed SAE-AISI 8630 is SAE-AISI 8630 steel in the annealed condition. The graph bars on the material properties cards below compare annealed SAE-AISI 8630 to: SAE-AISI wrought steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

160

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

24 %

Fatigue Strength

260 MPa 37 x 103 psi

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

340 MPa 50 x 103 psi

Tensile Strength: Ultimate (UTS)

540 MPa 78 x 103 psi

Tensile Strength: Yield (Proof)

360 MPa 52 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

410 °C 780 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

39 W/m-K 22 BTU/h-ft-°F

Thermal Expansion

11 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.3 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.6 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.5 kg CO2/kg material

Embodied Energy

20 MJ/kg 8.7 x 103 BTU/lb

Embodied Water

50 L/kg 5.9 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

110 MJ/m3

Resilience: Unit (Modulus of Resilience)

340 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

19 points

Strength to Weight: Bending

19 points

Thermal Diffusivity

10 mm2/s

Thermal Shock Resistance

18 points

Alloy Composition

Iron (Fe)Fe 96.8 to 97.9
Manganese (Mn)Mn 0.7 to 0.9
Nickel (Ni)Ni 0.4 to 0.7
Chromium (Cr)Cr 0.4 to 0.6
Carbon (C)C 0.28 to 0.33
Silicon (Si)Si 0.15 to 0.35
Molybdenum (Mo)Mo 0.15 to 0.25
Sulfur (S)S 0 to 0.040
Phosphorus (P)P 0 to 0.035

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A752: Standard Specification for General Requirements for Wire Rods and Coarse Round Wire, Alloy Steel

ASTM A322: Standard Specification for Steel Bars, Alloy, Standard Grades

Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015