Annealed (+A) 1.4923 Stainless Steel
EN 1.4923 +A steel is EN 1.4923 stainless steel in the annealed condition. It has the lowest strength and highest ductility compared to the other variants of EN 1.4923 stainless steel. The graph bars on the material properties cards below compare EN 1.4923 +A steel to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
270
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
21 %
Fatigue Strength
300 MPa 44 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
540 MPa 79 x 103 psi
Tensile Strength: Ultimate (UTS)
870 MPa 130 x 103 psi
Tensile Strength: Yield (Proof)
470 MPa 68 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Maximum Temperature: Corrosion
380 °C 720 °F
Maximum Temperature: Mechanical
740 °C 1360 °F
Melting Completion (Liquidus)
1450 °C 2650 °F
Melting Onset (Solidus)
1410 °C 2570 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
24 W/m-K 14 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.3 % IACS
Otherwise Unclassified Properties
Base Metal Price
8.0 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
2.9 kg CO2/kg material
Embodied Energy
41 MJ/kg 18 x 103 BTU/lb
Embodied Water
100 L/kg 12 gal/lb
Common Calculations
PREN (Pitting Resistance)
15
Resilience: Ultimate (Unit Rupture Work)
150 MJ/m3
Resilience: Unit (Modulus of Resilience)
570 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
31 points
Strength to Weight: Bending
26 points
Thermal Diffusivity
6.5 mm2/s
Thermal Shock Resistance
30 points
Alloy Composition
| Fe | 83.5 to 87.1 | |
| Cr | 11 to 12.5 | |
| Mo | 0.8 to 1.2 | |
| Mn | 0.4 to 0.9 | |
| Ni | 0.3 to 0.8 | |
| V | 0.25 to 0.35 | |
| Si | 0 to 0.5 | |
| C | 0.18 to 0.24 | |
| P | 0 to 0.025 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10302: Creep resisting steels, nickel and cobalt alloys
EN 10269: Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
Creep-Resistant Steels, Fujio Abe et al. (editors), 2008
Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010