Annealed (A or TB00) C15000 Copper
TB00 C15000 copper is C15000 copper in the TB00 (solution heat treated) temper. It has the lowest strength and highest ductility compared to the other variants of C15000 copper. The graph bars on the material properties cards below compare TB00 C15000 copper to: wrought coppers (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
54 %
Poisson's Ratio
0.34
Shear Modulus
43 GPa 6.3 x 106 psi
Shear Strength
150 MPa 21 x 103 psi
Tensile Strength: Ultimate (UTS)
200 MPa 29 x 103 psi
Tensile Strength: Yield (Proof)
45 MPa 6.5 x 103 psi
Thermal Properties
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C 390 °F
Melting Completion (Liquidus)
1080 °C 1980 °F
Melting Onset (Solidus)
980 °C 1800 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
370 W/m-K 210 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
93 % IACS
Electrical Conductivity: Equal Weight (Specific)
93 % IACS
Otherwise Unclassified Properties
Base Metal Price
31 % relative
Density
9.0 g/cm3 560 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
43 MJ/kg 19 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
80 MJ/m3
Resilience: Unit (Modulus of Resilience)
8.7 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
6.2 points
Strength to Weight: Bending
8.5 points
Thermal Diffusivity
110 mm2/s
Thermal Shock Resistance
7.3 points
Alloy Composition
| Cu | 99.8 to 99.9 | |
| Zr | 0.1 to 0.2 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993