Annealed M34 Tool Steel

Annealed SAE-AISI M34 is SAE-AISI M34 steel in the annealed condition. The graph bars on the material properties cards below compare annealed SAE-AISI M34 to: tool steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

240

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Poisson's Ratio

0.29

Shear Modulus

77 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

800 MPa 120 x 103 psi

Thermal Properties

Latent Heat of Fusion

270 J/g

Melting Completion (Liquidus)

1540 °C 2810 °F

Melting Onset (Solidus)

1500 °C 2730 °F

Specific Heat Capacity

450 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

24 W/m-K 14 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Otherwise Unclassified Properties

Base Metal Price

32 % relative

Density

8.2 g/cm3 510 lb/ft3

Embodied Carbon

9.5 kg CO2/kg material

Embodied Energy

140 MJ/kg 59 x 103 BTU/lb

Embodied Water

150 L/kg 18 gal/lb

Common Calculations

PREN (Pitting Resistance)

35

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

27 points

Strength to Weight: Bending

23 points

Thermal Diffusivity

6.7 mm2/s

Thermal Shock Resistance

25 points

Alloy Composition

Iron (Fe)Fe 71.3 to 76.5
Molybdenum (Mo)Mo 7.8 to 9.2
Cobalt (Co)Co 7.8 to 8.8
Chromium (Cr)Cr 3.5 to 4.0
Vanadium (V)V 1.9 to 2.3
Tungsten (W)W 1.4 to 2.1
Carbon (C)C 0.85 to 0.92
Silicon (Si)Si 0.2 to 0.45
Manganese (Mn)Mn 0.15 to 0.4
Nickel (Ni)Ni 0 to 0.3
Copper (Cu)Cu 0 to 0.25
Phosphorus (P)P 0 to 0.030
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A600: Standard Specification for Tool Steel High Speed

Tool Steels, 5th ed., George Roberts et al., 1998

Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996