Annealed (OS025) C33000 Brass
OS025 C33000 brass is C33000 brass in the OS025 (annealed to 0.025mm grain size) temper. The graph bars on the material properties cards below compare OS025 C33000 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 15 x 106 psi
Elongation at Break
50 %
Poisson's Ratio
0.31
Rockwell F Hardness
75
Rockwell Superficial 30T Hardness
37
Shear Modulus
40 GPa 5.9 x 106 psi
Shear Strength
260 MPa 37 x 103 psi
Tensile Strength: Ultimate (UTS)
360 MPa 52 x 103 psi
Tensile Strength: Yield (Proof)
150 MPa 22 x 103 psi
Thermal Properties
Latent Heat of Fusion
180 J/g
Maximum Temperature: Mechanical
130 °C 270 °F
Melting Completion (Liquidus)
940 °C 1720 °F
Melting Onset (Solidus)
900 °C 1660 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
120 W/m-K 67 BTU/h-ft-°F
Thermal Expansion
20 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
26 % IACS
Electrical Conductivity: Equal Weight (Specific)
29 % IACS
Otherwise Unclassified Properties
Base Metal Price
24 % relative
Density
8.2 g/cm3 510 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
45 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
140 MJ/m3
Resilience: Unit (Modulus of Resilience)
110 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
12 points
Strength to Weight: Bending
14 points
Thermal Diffusivity
37 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Cu | 65 to 68 | |
| Zn | 30.8 to 34.8 | |
| Pb | 0.25 to 0.7 | |
| Fe | 0 to 0.070 | |
| res. | 0 to 0.4 |
All values are % weight. Ranges represent what is permitted under applicable standards.