Annealed (OS025) C41300 Brass

OS025 C41300 brass is C41300 brass in the OS025 (annealed to 0.025mm grain size) temper. It has the second lowest strength and second highest ductility compared to the other variants of C41300 brass. The graph bars on the material properties cards below compare OS025 C41300 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

110 GPa 16 x 106 psi

Elongation at Break

42 %

Poisson's Ratio

0.33

Rockwell F Hardness

62

Rockwell Superficial 30T Hardness

22

Shear Modulus

42 GPa 6.1 x 106 psi

Shear Strength

240 MPa 35 x 103 psi

Tensile Strength: Ultimate (UTS)

310 MPa 46 x 103 psi

Tensile Strength: Yield (Proof)

130 MPa 20 x 103 psi

Thermal Properties

Latent Heat of Fusion

200 J/g

Maximum Temperature: Mechanical

180 °C 360 °F

Melting Completion (Liquidus)

1040 °C 1900 °F

Melting Onset (Solidus)

1010 °C 1850 °F

Specific Heat Capacity

380 J/kg-K 0.092 BTU/lb-°F

Thermal Conductivity

130 W/m-K 77 BTU/h-ft-°F

Thermal Expansion

18 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

30 % IACS

Electrical Conductivity: Equal Weight (Specific)

31 % IACS

Otherwise Unclassified Properties

Base Metal Price

29 % relative

Density

8.7 g/cm3 550 lb/ft3

Embodied Carbon

2.7 kg CO2/kg material

Embodied Energy

44 MJ/kg 19 x 103 BTU/lb

Embodied Water

320 L/kg 38 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

110 MJ/m3

Resilience: Unit (Modulus of Resilience)

81 kJ/m3

Stiffness to Weight: Axial

7.2 points

Stiffness to Weight: Bending

18 points

Strength to Weight: Axial

10 points

Strength to Weight: Bending

12 points

Thermal Diffusivity

40 mm2/s

Thermal Shock Resistance

11 points

Alloy Composition

Copper (Cu)Cu 89 to 93
Zinc (Zn)Zn 5.1 to 10.3
Tin (Sn)Sn 0.7 to 1.3
Lead (Pb)Pb 0 to 0.1
Iron (Fe)Fe 0 to 0.050
Residualsres. 0 to 0.5

All values are % weight. Ranges represent what is permitted under applicable standards.